Ferrovanadium Nitride FERVANIT®

FERVANIT® is a composition alloy, which produced by nitriding of ferrovanadium powder under high pressure (8MPa) and temperature ~1500 °C. The principal phase of FERVANIT® is vanadium nitride with iron binder. Deep research of SHS-process allowed to get unique alloy. The combination of high density with maximum nitrogen content was first possible in Ferrovanadium nitride FERVANIT®. It is supplied in the lump form and can be loaded both in furnace and in ladle. Our product has low melting point ~1450 oC, high density 6,0-6,5 g/cm3, maximum nitrogen content, absence of open porosity, crashing strength is more than 200 MPa.At the customer's request we can also produced ferrovanadium nitride for cored wire production. In this case high grade ferrovanadium (70-80 % V) is nitriding; during burning synthesis process sintered composition is produced, which after being powdered is used as filling agent in flux cored wire.